Electric Vehicle Electrophoresis Paint Totally Enclosed Multi Isocyanates

Product Categories

ED Paint [23]
Cathodic Electrodeposition Paint [19]
Electrophoretic Coating [24]
ED Black Coating [30]
E Coating Car Body [14]
E Coat Car Coating [8]
Auto Parts ED Painting [9]
Home Appliances ED Paint [10]
Grey Electrophoretic Coating [15]
White Electrophoretic Coating [13]
Colour Electrophoresis Coating [10]
High Anticorrosive Performance Electrophoretic Paint [13]
High Weatherability Electrophoretic Paint [8]
High - Swimming Penetration Electrophoresis Paint [7]
Low Temperature Curing Electrophoresis Paint [6]
Engineering Machinery / Agricultural Mechanical Electrophoretic Paint [19]
Electrophoretic Paint For Casting [7]

HLS Coatings （Shanghai）Co.Ltd

Trust Seal

Verified Supplier

Credit Check

Supplier Assessment

Contact Now

Electric Vehicle Electrophoresis Paint Totally Enclosed Multi Isocyanates

Name: Electric Vehicle Electrophoresis Paint Totally Enclosed Multi Isocyanates
Brand: HAOLISEN
Price: 1 USD

Brand Name : HAOLISEN

Model Number : HR-4000BLB/HR-6000

Certification : IATF16949 , ISO9001

Place of Origin : Shanghai China （Mainland）

MOQ : Negotiation

Price : Negotiation

Supply Ability : 200 Tons Per Day

Delivery Time : 30-60 Days

Packaging Details : 50kg、60 kg、200kg、1000kg packaging barrels

Application field : lectric vehicle

Performance : beautiful appearance

Cooperation case : SUNRA LUYUAN

main ingredients : totally enclosed multi-isocyanates

Contact Now

Solution for the electric vehicle electrophoresis paint

Product Introduction:

HR-4000BLB/HR-6000 the bottom of one black cathode electrophoretic coating, is HLS Paint (Shanghai) Co., Ltd., the eighth generation of independent research and development of electrophoretic coating. This coating by epoxy acrylate modified, the film also has excellent corrosion resistance and weatherability, smooth appearance and full, suitable as a base topcoat system. In addition, the lead, cadmium, chromium, mercury and other heavy metals, two-component, water dispersible resin, at the same time, previous generations of the product characteristics, have good adaptability to the galvanized steel, almost can be applied to all metal coating,

such as: cold hot rolled steel, galvanized steel, aluminum, zinc Aluminum Alloy plate, stainless steel plate.

This product features shown below:


Good stability of bath can adaptable for a longer updating cycle. 

High penetration and good uniformity of internal and external. 

Have excellent corrosion resistance and weathering resistance, especially suitable for the bottom surface of a painting

Main ingredients:

Solvent: alcohol ether

Additives: surface active agent, prevent shrinkage cavity agent

Pigment: carbon black, kaolin, antirust pigment

Filling tank proportion and method

⑴ Bath preparation

Ratio:

Resin 10500.00-1400.00

Paste 175.00

NHF-01 2.00

DI water 1785.00

Total 3362.00-3012.00

⑵ Ripening conditions

Sample quantity: 3000～4500g
Container: 5L (Diameter 16cm)

Tank temperature:30 ±2 ℃

Time: 24～48Hr

Mixed conditions: impeller diameter 8cm (speed 200rpm)

Product film performance :

Project		Indicator	Test standard
Appearance	Normal / Abnormal	Normal	Ocular estimate
Hardness	≥	2H	GB/T 6739
Cup drawing	mm,≥	7	GB/T 9753
Adhesion	level	0	GB/T 9286
Flexibility	mm	1	GB/T 1731
Impact	Kg.cm	50	GB/T 1732
Gloss	60°	60-90	GB/T 9754
Water resistance	h,(23±2)℃ ≥	240	GB/T 1733
Acid resistance	h(0.05N H2SO4) ≥	72	GB/T 9274
Alkali resistance	h(0.1N NaOH) ≥	72	GB/T 9274
Weather resistanc	h,(film thickness ≥ 20μm)≥	600	GB/T 165
*Salt spray resistance	film thickness ≥ 20μm	800	GB/T 1771

* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.